Stress Relief: (1) Uniform heating of a structure or portion thereof to a sufficient temperature to relieve the major portion of the residual stresses, followed by uniform cooling. (2) The reduction of residual stress in a metal part by heating it to a given temperature and holding it there for a suitable length of time. This treatment is used to relieve stresses caused by welding, cold working, machining, casting, and quenching.

Quality Statement: ThermoFusion is committed to customer satisfaction through excellence in heat treating and brazing services. ThermoFusion and its employees take pride in the quality of their work and are dedicated to improving.

Equilibrium Diagram: A graphical representation of the temperature, pressure and composition limits of phase fields in an alloy system as they exist under conditions of complete equilibrium. In metal systems, pressure is usually considered constant.

Tempering: Reheating quenched steel to a temperature below the critical range, followed by any desired rate of cooling. Tempering is done to relieve quenching stresses, or to develop desired strength characteristics.

Ductility: The property of a material to deform permanently, or to exhibit plasticity without rupture, while under tension.

Cast Iron: Iron containing 2 to 4.5 percent carbon, silicon, and other trace elements. It is used for casting objects into molds. Cast iron is somewhat brittle.

Martempering (Marquenching): A method of hardening steel by quenching from the austenitizing temperature into salt, and then cooling in air and then tempering. The interrupted cooling allows for reduced distortion in some situations.

Austempering: Hardening steel by quenching from the austenitizing temperature into salt, and transforming the austenite into bainite. Austempering often increases ductility and toughness.

Normalizing: Heating a ferrous alloy to a suitable temperature above the transformation range and then cooling in below the transformation range.

Decarburization: When steel is heated in the presence of a medium such as air, oxygen or hydrogen, there is a loss of carbon at the surface of the steel. This loss of carbon, or decarburization, results in a reduction of surface hardness of the steel.

Air Hardening Steel: An alloy steel which does not require quenching from a high temperature to harden, but which is hardened by simply cooling in air from above its critical temperature range.

Austenite: A solid solution of iron and carbon (and sometimes other elements), obtained by heating the material to a temperature above the upper critical temperature (or transformation temperature).

Counterborevs countersink

Oct 21, 2005 — A #29 drill bit falls between a 9/64" and a 1/8" drill bit in size. If you don't have the correct size, it's always better to go a little larger in size, so ...

Induction Hardening: A surface hardening process in which only the surface layer of a suitable ferrous work piece is heated by electromagnetic induction to above the upper critical temperature and immediately quenched.

Cryogenic Treatment: Often called cold treatment or deep freezing. Steel is exposed to suitable subzero temperatures (-85 C or lower) for the purpose of obtaining desired conditions or properties such as dimensional or micro- structural stability. May also reduce retained austenite.

Brinnell Hardness Test: A test for determining the hardness of a material by forcing a hard steel or carbide ball of specified diameter into it under a specified load. The result is expressed as the Brinell Hardness number, which is the value obtained by dividing the applied load in kilograms by the surface area of the resulting impression in square millimeters.

C6 is the epitome of permanent, proprietary ceramic coating technology and protective prowess. C6 delivers the utmost in gloss, smoothness, and self-cleaning ...

Stress: The load per unit of area on a stress-strain diagram. Tensile stress refers to an object loaded in tension, denoting the longitudinal force that causes the fibers of a material to elongate. Compressive stress refers to a member loaded in compression, which either gives rise to a given reduction in volume or a transverse displacement of material. Shear stress refers to a force that lies in a parallel plane. The force tends to cause the plane of the area involved to slide on the adjacent planes. Torsional stress is a shearing stress that occurs at any point in a body as the result of an applied torque or torsional load.

Austenitizing: The process of forming austenite by heating an iron/carbon alloy above its transformation temperature. The austenitizing temperature varies for different grades of carbon, alloy and tool steels.

Homogeneous Carburizing: Use of carburizing process to convert low-carbon ferrous to allow one of uniform and higher carbon content throughout the section.

Bark: An older term used to describe the decarburized skin that develops on steel bars heated in a non-protective atmosphere.

Hand Saws - Hand saws are manual saws used for cutting wood by hand. They are suitable for small to medium-sized wood cutting tasks, such as trimming, ...

Aging: The process of holding metals at room temperature or at a predetermined temperature for the purpose of increasing their hardness and strength by precipitation; aging is also used to increase dimensional stability in metals such as castings.

Drawing: A term used interchangeably with tempering, and refers to reheating hardened (and usually quenched) steel to a temperature below the lower critical temperature, followed by cooling. Drawing slightly reduces the hardness of the steel, but increases ductility and makes the part less brittle.

Hydrogen Brazing: The joining of materials using an alloy, above 450C and in a hydrogen environment. The hydrogen acts as a flux or cleaning agent for the surfaces being joined.

Magnetic Annealing: Annealing a part, usually made of a high-nickel alloy, in order to change its magnetic properties, including magnetic permeability.

Counterboretool

Fracture: A ruptured surface of metal that shows a typical crystalline pattern. Fatigue fractures, however, often display a smooth, clam-shell appearance.

Anneal: To heat and then cool a material, or for treatments intended to alter the mechanical or physical properties to produce a definite microstructure. Property changes include removing stress, inducing softness, altering ductility or toughness, or changing electric or magnetic properties.

Knoop Hardness: Microhardness determined from the resistance of metal to indentation by a pyramidal diamond indenter, having edge angels of 172, 30 and 130 degrees, making a rhombohedral impression with one long and one short diagonal.

Ball Diameter, 1 7/8 inch. Thickness Range, 3/8 inch to 3/4 inch. Finish, Chrome. GTW, 2,000. Shank Diameter, 3/4 inch. Shank Length, 1 9/16 inch. List Price: ...

Carburizing: Adding carbon to the surface layer of steel by heating the steel below its melting point, while in contact with carbonaceous solids, liquids or gases.

Counterboredrawing

What Does Work Hardening Mean? Work hardening, is the strengthening of a metal by plastic deformation. In the plastic region, the true stress increases ...

Enter Nick Foley and Andrew Savvas, owners of Camberwell's Gloria's wine bar. The duo has reinvigorated part of the exemplary art-deco structure into a double- ...

You don't have to have a license to pilot a bore, but if you want to create a flat recessed opening at the top of hole for your socket head cap screw to sit in flush with the top of your piece, you need a counterbore with or without a pilot. KBC Tools & Machinery's counterbores come in blade type, cap screw, and interchangeable pilots for all your counterboring needs. KBC has counterbores available in imperial, numbered, and metric sizes from Brand KBC, APT, and Rock River Tool. KBC - All Counterbores...All The Time

Sep 11, 2019 — EDM machine technology has spawned a world of new applications wherein increased importance is placed on the graphite electrode material ...

Racking: A term used to describe the placing of parts to be treated or joined on a rack or tray. This is done to keep parts in a proper position to avoid heat-related distortions and to keep the parts separated. See fixturing.

Forging: The shaping of metal by hammering or pressing. Although forging may be used to shape malleable metals in the cold state, the application of heat increases plasticity and permits greater deformation without inducing undue strain in the metal.

Oil Quenching: Hardening of carbon steel in an oil bath. Oils are categorized as conventional, fast, martempering or hot quenching.

Critical Temperature: The preferred term used by metallurgists is transformation temperature. The lower A1 and the upper A3 temperatures are the boundaries of the transformation range in which ferrite transformations into austenite.

Vacuum Furnace: A furnace using low atmospheric pressures instead of a protective gas atmosphere. Vacuum furnaces are categorized as hot wall or cold wall, depending on the location of the heating and unsulating components.

Beta Annealing: Producing a beta phase by heating certain titanium alloys in the appropriate temperature range, and then cooling at a rate to prevent its decomposition.

Diffusion: The process of inter-mingling atoms or other particles within a solution. In solids, it is a slow movement of atoms from areas of high concentration toward areas of low concentration. The process may be (a) migration of interstitial atoms such as carbon, (b) movement of vacancies, or (c) direct exchange of atoms to neighboring sites.

Flame Hardening: A heat treatment method used to harden the surface of some parts via the use of a flame, followed by an oil quench.

Oct 1, 2014 — Cutting an internal keyway in a shaper is going to require the use of a "poke bar" which is roughly equivalent to a boring bar in a lathe, and this will be the ...

Repository files navigation ... Performance Co-Pilot (PCP) provides a framework and services to support system-level performance monitoring and management. It ...

Hardenability: The property that determines the depth and distribution of hardness in a ferrous alloy induced by heating or quenching.

Equilibrium: A condition of balance in which all the forces or processes that are present are counterbalanced by equal or opposite forces or processes where the condition appears to be one of rest rather than of change.

Thermal Stress: Shear stress that is induced in a material due to unequal heating or cooling rates. The difference of expansion and contraction between the interior and exterior surfaces of a metal that is being heated or cooled is an example.

Rockwell Hardness Test: An indentation hardness test based on the depth of penetration of a specified penetrator into the specimen under certain arbitrarily fixed conditions.

Counterborehole

Oxidation: (1) A reaction in which there is an increase in valence resulting from a loss of electrons. (2) A corrosion reaction in which the corroded metal forms an oxide; usually applied to reaction with a gas containing elemental oxygen, such as air.

Soaking: A prolonged heating of metal at a predetermined temperature to create a uniform temperature throughout its mass.

Precipitation Hardening: A process of hardening an alloy by heat treatment, in which a constituent precipitates from a supersaturated solid solution while at room temperature or at some slightly elevated temperature.

Ferrite: A magnetic form of iron. A solid solution in which alpha iron is the solvent, characterized by a body-centered cubic crystal structure.

Kennametal® 6086562 GOmill™ GP Center Cutting General Purpose Square End Mill, 1/8 in Dia Cutter, 1/2 in Length of Cut, 4 Flutes, 1/8 in Dia Shank, ...

Stainless Steel: An alloy of iron containing at least 11 percent chromium and sometimes nickel that resists almost all forms of rusting and corrosion.

Fixturing: The placing of parts to be heat treated in a constraining or semi-constraining apparatus to avoid heat-related distortions. See racking.

Age Softening: Spontaneous decrease of strength and hardness that takes place at room temperature in certain strain-hardened alloys, especially those of aluminum.

Tool Steel: A special group of steels that are designed for specific uses such as heat-resistant steels that can be heat treated to produce certain properties, mainly hardness and wear resistance.

Hardening: Increasing hardness of metals by suitable treatment, usually involving heating and cooling. More specific terms include age hardening, case hardening, flame hardening, induction hardening, precipitation hardening, and quench hardening.

Spheroidizing: A process in which carbon steel is held for a period of time at just under the transformation temperature. An aggregate of globular carbide is formed from other microstructures such as pearlite.

Counterboredrill

Thermal Expansion: The increase of the dimension of a material that results from the increased movement of atoms caused by increased temperature.

Steel: An alloy of iron and less than 2 percent carbon plus some impurities and small amounts of alloying elements is known as plain carbon steel. Alloy steels contain substantial amounts of alloying elements such as chromium or nickel besides carbon.

Counterborekit

Maraging: A precipitation hardening treatment applied to a special group of iron-0base alloys to precipitate one or more intermetallic compounds in a matrix of essentially carbon free martensite.

Car Furnace: A batch-type furnace using a car on rails to enter and leave the furnace area. Car furnaces are used for lower stress relieving ranges.

Inclusions: Particles of impurities that are usually formed during solidification and are usually in the form of silicates, sulfides, and oxides.

Nitriding: The process of adding nitrogen to the surface of a steel. Nitriding develops a very hard case after a long time at comparatively low temperature. Benefits include an improved wear surface and corrosion resistance, which may increase the life of the part.

Nitrocarburizing: Any of several processes in which both nitrogen and carbon are absorbed into the surface layers of a ferrous material. Nitrocarburizing is performed primarily to provide an anti-scuffing surface layer and to improve fatigue resistance.

CounterboreBit

Quenching: The process of rapid cooling metal alloys for the purpose of hardening. Quenching media include air, oil, water, molten metals, and fused salts.

Hardness: The property of a metal to resist being permanently deformed. This is divided into three categories: the resistance to penetration, abrasion, and elastic hardness.

Solution Heat Treatment: Heating an alloy to a suitable temperature, holding at that temperature long enough to cause one or more constituents to enter into solid solution, and then cooling rapidly enough to hold these constituents in solution.

Alloy: A substance that has metallic properties and is composed of two or more chemical elements of which at least one is a metal. Aluminum Dip Brazing: The joining of aluminum parts using an aluminum alloy, above 450C and in a salt environment. The salt acts as a flux or cleaning agent for the surfaces being joined.

Atmosphere: The gaseous environment in which the metal being treated is heated for processing. Atmospheres are used to protect from chemical change, or to alter the surface chemistry of steel through the addition or removal of carbon, nitrogen, hydrogen, and oxygen and to add certain metallic elements as chromium, silicon, sulphur, etc.

Counterboresymbol

Neutral Hardening: To harden carbon steel parts by heating them to the proper temperature in atmospheres such as pure nitrogen, nitrogen and natural gas, or nitrogen-methanol, followed by quenching.

Macroscopic: Structural details on an object that are large enough to be observed by the naked eye or with low magnification (about 10x).

Liquid Penetrant Inspection: A type of nondestructive inspection that locates discontinuities that are open to the surface of a metal by first allowing a penetrating dye or fluorescent liquid to infiltrate the discontinuity, removing the excess penetrant, and then applying a developing agent that causes the penetrant to seep back out of the discontinuity and register as an indication. Liquid penetrant inspection is suitable for both ferrous and nonferrous materials, but is limited to the detection of open surface discontinuities in nonporous solids.

Hydrogen Embrittlement: The brittleness induced in steel by the absorption of atomic hydrogen, most commonly from a pickling or plating operation.

Brittleness: The property of materials that will not deform under load but tend to break suddenly; for example, cast iron and glass are brittle. Brittleness is the property opposite to plasticity. Bright Annealing / Bright Hardening: Annealing in a protective medium or atmosphere to prevent discoloration of the bright surface.

Controlled Cooling: Cooling from an elevated temperature in a pre-determined manner, to avoid hardening, cracking or internal damage, or to produce desired mecrostructure or mechanical properties.

Eutectic: (1) An isothermal reversible reaction in which a liquid solution is converted into two or more intimately mixed solids on cooling, the number of solids formed being the same as the number of components in the system. (2) An alloy having the composition indicated by the eutectic point on an equilibrium diagram. (3) An alloy structure of intermixed solid constituents formed by eutectic reaction.

Transformation Temperature: The temperatures at which one phase transforms into another phase; for example, ferrite or alpha iron transforms into austenite or gamma iron.

Martensite: An unstable constituent that is formed by heating and quenching steel. It is formed without diffusion and only below a certain temperature. Martensite is the hardest of the transformation products of austenite, having an acicular, or needlelike, microstructure.

Toughness: Generally measured in terms of notch toughness, which is the ability of a metal to resist rupture from impact loading when a notch is present. A standard test specimen containing a prepared notch is inserted into the vise of a testing machine. This devise, called the Izod-Charpy testing machine, consists of a weight on a swinging arm. The arm or pendulum is released, strikes the specimen, and continues to swing forward. The amount of energy absorbed by the breaking of the specimen is measured by how far the pendulum continues to swing.

Strength: The ability of a metal to resist external forces. This is called tensile, compressive, or shear strength; depending on the load. See stress.

Vacuum Brazing: The joining of materials using an alloy, above 450C and in a vacuum environment. The vacuum acts as a flux or cleaning agent for the surfaces being joined.

Dip Brazing: The joining of aluminum parts using an aluminum alloy, above 450C and in a salt environment. The salt acts as a flux or cleaning agent for the surfaces being joined.

Brazing: The joining of two or more metals with the use of a dis-similar material or alloy above 450C. Brazing may be done in air, or in a protective atmosphere such as vacuum or hydrogen.

Case Hardening: A process in which a ferrous alloy is hardened so that the surface layer or case is made considerably harder than the interior or core. Some case-hardening processes are carburizing, cyaniding, carbonitriding, carbo-nitriding, nitriding, flame hardening, and induction hardening.