Workhardening therapy

My left earbud recently broke mid-wire: the bit that I like to fiddle with and bend. I fixed it, but I was wondering whether there are metals that don't work harden, or resistant to it?

What isworkhardening in occupational therapy

Is there a way that you can treat normal metal to prevent it from, or at least reduce the effects of, work hardening. Can these be used in headphones commercially?

Unseen hand is pretty good for healing but soul spiral can do some crazy damage seems to have a pretty good prof coefficient and the barrier ...

Work hardening leads to essentially hardening or strengthening till no further ductility is produced or material fractures or fails. If the material doesnt work harden or if there is no plasticity it is going to fail by brittle fracture at yield point.

As someone pointed out , Annealing is majorly used to soften a material so that its more workable. So essentially if you want to reverse the effects of work hardening this is the only route that is viable.

What isworkhardening in Engineering

the cutting surfaces on a vertical end mill bit ( are for milling ) are on its sides , designed for cutting horizontally , a drill bit ( are for ...

Just to add to the other answers, you unfortunately will have to replace the whole wire/earbud set. Melting the wire will only fuse the different isolated wires that exist in one cord, and you will have an at best dysfunctional if not dangerous product that works in only one ear. Sorry to be the bearer of bad news.

work-hardening doesn't persist if the service temperature is above 1/3rd to 1/2 of the melt temperature- at which thermally-activated diffusion effects are sufficiently strong to relieve the dislocation pileups via dislocation climb. a thick lead wire cannot be work-hardened at room temperature because its melt temperature is in this range- but neither can it be used as a spring to help hold the earphone in place, for this same reason: it creeps significantly at room temperature.

As for metals that can recover from being yielded there are shape-memory alloys, though I think they would be cost prohibitive.

Workhardening examples

Of course, if by fiddle with and bend you mean deform past the elastic limit so that there is a kink, then you are inherently exceeding the yield stress every cycle and micro cracks will propagate very quickly. If this is what you'd like to due to your cords and would like a cord to survive this treatment, I would design such a cord with thin braided wires that were surrounded by a self-healing polymer. This would allow you to plastically deform the cord and have the cord heal itself.

If the stress on the wire at the edge is below the endurance limit then the wire could be bent back and forth indefinitely. One way to reduce stress and allow for more flexible wires is to use braided wires. This works by reducing the cross section of each strand and thus reducing the amount of strain required to produce a certain bend radius.

Stack Exchange network consists of 183 Q&A communities including Stack Overflow, the largest, most trusted online community for developers to learn, share their knowledge, and build their careers.

Work hardenreddit

The wires you mention can be produced/manufactured only if they show plasticity(or work hardening) in the first place, if they were perfectly elastic they couldn't be used due to risk of brittle fracture or low toughness.

Workhardening metal

Work hardenmeaning

Oct 30, 2023 — A lathe is a machine that cuts materials like wood, metal, and plastic into desired shapes by spinning the workpiece in a circular motion at a high speed.

Cricut Venture is perfect for small business and big projects. Cut materials up to 25 inches wide at commercial cutting speeds. Start crafting Today!

ZYLtech Arduino UNO Compatible CNC Kit w/ Controller + Shield + Nema 23 Stepper Motors + PSU + Toshiba TB6600 $107.95 - $122.45

G2S TOBEQ Inc. is a wholesale distributor of tools and equipment serving the automotive, heavy-duty, industrial, agricultural and marine industries. We ...

My left earbud recently broke mid-wire: the bit that I like to fiddle with and bend. I fixed it, but I was wondering whether there are metals that don't work harden, or resistant to it?

Harvey Building Products Corporation | 571 followers on LinkedIn. Manufacturer of high-performing, custom-made windows and doors. | Harvey Building Products ...

Work hardening does not cause things to break, but in fact will cause them to resist further plastic deformation increasing their strength. Wires bent back and forth may eventually break due to fatigue. The material at the edge is compressed and stretched resulting in fatigue. How much cyclic stress there is determines how many cycles the material can last its fatigue limit.