At high temperatures WC decomposes to tungsten and carbon and this can occur during high-temperature thermal spray, e.g., in high velocity oxygen fuel (HVOF) and high energy plasma (HEP) methods.

Tungsten carbide has a high melting point at 2,870 °C (5,200 °F), a boiling point of 6,000 °C (10,830 °F) when under a pressure equivalent to 1 standard atmosphere (100 kPa), a thermal conductivity of 110 W·m−1·K−1, and a coefficient of thermal expansion of 5.5 µm·m−1·K−1.

Oxidation of WC starts at 500–600 °C (932–1,112 °F). It is resistant to acids and is only attacked by hydrofluoric acid/nitric acid (HF/HNO3) mixtures above room temperature. It reacts with fluorine gas at room temperature and chlorine above 400 °C (752 °F) and is unreactive to dry H2 up to its melting point. Finely powdered WC oxidizes readily in hydrogen peroxide aqueous solutions. At high temperatures and pressures it reacts with aqueous sodium carbonate forming sodium tungstate, a procedure used for recovery of scrap cemented carbide.

By entering in your mobile number above, you agree to receive recurring marketing text messages (e.g. cart reminders), which may be automated, to the mobile number used at opt-in from Kreg Tool. Consent is not a condition of purchase. Msg frequency may vary. Msg & data rates may apply. Reply HELP for help and STOP to cancel. See Terms and Conditions & Privacy Policy.

First, align your cuts quickly and precisely with the cutline indicators. Cutline indicators make alignment to your pencil marks easy, so you can work confidently knowing you’ll make the cut exactly where you need it. Then secure the guide to your material using the low-profile GripMaxx™ clamps that are built right into the guide. And now you're ready to make a cut!

Tungsten carbide is prepared by reaction of tungsten metal and carbon at 1400–2000 °C. Other methods include a patented lower temperature fluid bed process that reacts either tungsten metal or blue WO3 with CO/CO2mixture and H2 between 900 and 1200 °C.

Make perfectly straight cuts up to 8 feet in sheet goods with guided cutting Cut sheet goods down to size with precision and ease by using the Kreg® Straight Edge Guide. Work with material up to 8 feet and get the cuts you need — whether you're using a circular saw, jigsaw, or trim router. (Works with most brands.)

Within the field of engineering materials, cemented carbides play a crucial role as they combine high hardness and strength with good toughness within a wide property range, and thus constitute the most versatile hard materials group for engineering and tooling applications.

By entering your email address above, you agree to receive marketing messages from Kreg about new products, promotions and projects. You may update your email preferences at any time.

First, align your cuts quickly and precisely with the cutline indicators. Cutline indicators make alignment to your pencil marks easy, so you can work confidently knowing you’ll make the cut exactly where you need it. Then secure the guide to your material using the low-profile GripMaxx™ clamps that are built right into the guide. And now you're ready to make a cut!

Make perfectly straight cuts up to 8 feet in sheet goods with guided cutting Cut sheet goods down to size with precision and ease by using the Kreg® Straight Edge Guide. Work with material up to 8 feet and get the cuts you need — whether you're using a circular saw, jigsaw, or trim router. (Works with most brands.)

Tungsten carbide is extremely hard, ranking about 9 on Mohs scale, and with a Vickers number of around 2600. It has a Young's modulus of approximately 530–700 GPa, a bulk modulus of 630–655 GPa, and a shear modulus of 274 GPa. It has an ultimate tensile strength of 344 MPa, an ultimate compression strength of about 2.7 GPa and a Poisson's ratio of 0.31.

Mechanical properties reflect the ability of a material to withstand a force of a certain type that, however, when applied, requires a more accurate definition. For clarity there are various types of force to which the resistance is opposed, depending on the load conditions; for hard metals the most important resistances within mechanical properties are compression resistance traction, abrasion, fatigue and bump transversal breakage .:

The Kreg Straight Edge Guide XL offers an intuitive and approachable way to break down sheet goods. Your saw rides against the aluminum guide, allowing you to make straight and precise cuts. Guided cutting makes it easier than ever to see exactly where you'll cut so you can get the results you expect.

Cemented carbides, or hardmetals as they are often called, are materials made by "cementing" very hard tungsten monocarbide (WC) grains in a binder matrix of a tough cobalt or nickel alloy by liquid phase sintering.  Cemented carbides combine the high hardness and strength of metallic carbides (WC, TiC, TaC) or carbonitrides (eg TiCN) with the toughness and plasticity of a metallic alloy binder (Co, Ni, Fe), in which the hard particles are evenly distributed to form a metallic composite.  Tungsten carbide is the most metallic of the carbides, and by far the most important hard phase.  The more hard carbide particles are within the material, the harder it is but the less tough it behaves during loading; and, vice versa, significant increases in toughness are achieved by a higher amount of metallic binder at the expense of hardness.

There are two well-characterized compounds of tungsten and carbon, WC and tungsten semicarbide, W 2C. Both compounds may be present in coatings and the proportions can depend on the coating method.

Typically a Tungsten Carbide Hard Metal can have a hardness value of 1600 HV, whereas mild steel would be in the region of 160 HV a factor of 10 lower.

WC is readily wetted by both molten nickel and cobalt. Investigation of the phase diagram of the W-C-Co system shows that WC and Co form a pseudo binary eutectic. The phase diagram also shows that there are so-called η-carbides with composition (W,Co) 6C that can be formed and the brittleness of these phases makes control of the carbon content in WC-Co hard metals important.

Although called a hard metal, Tungsten Carbide is actually a composite material with hard particles of Tungsten Carbide embedded in a softer matrix of metallic Cobalt .

The Kreg Straight Edge Guide XL offers an intuitive and approachable way to break down sheet goods. Your saw rides against the aluminum guide, allowing you to make straight and precise cuts. Guided cutting makes it easier than ever to see exactly where you'll cut so you can get the results you expect.